Certificate
Cobalt, nickel-based alloys are commonly used in the dental industry to make dental restorations.
Cobalt, nickel-based alloys are commonly used in the dental industry to make dental restorations. Because of their good mechanical properties and biology compatibility, they have become the best economic substitutes for gold and silver based alloys ( precious metals ).
Currently, we offer StelliteC5 cobalt-based and StelliteN9 nickel-based alloys for porcelain-fused-to-metal alloys and StelliteC3 cobalt-based alloys for bracket alloys. For the health of users, our dental alloys do not contain beryllium, cadmium and other elements. In order to adapt to the development of technology, we also provide customers with alloy powder products suitable for 3D printing process.
In order to produce dental alloys with high standards and meeting customer requirements, Kennametal Stellite has obtained ISO 13485 medical system and CE certification, and completed FDA registration in the United States;
Main technical performance indicators:
|
Ingredient ( % ) |
Cobalt 57-61 |
chromium 25-29 |
Molybdenum 4-6 |
Tungsten 6-8 |
|
Beryllium ≤ 0.02 |
cadmium ≤ 0.02 |
Ni ≤ 0.1 |
— |
|
|
physical properties |
||||
|
Specified plastic elongation strength Rp0.2 |
≥ 270MPa |
|||
|
Elongation after fracture |
≥ 5 % |
|||
|
Hardness HV30 |
≥ 350 |
|||
|
Coefficient of thermal expansion |
( 14.2 ± 0.5 ) × 10-6K-1 |
|||
|
modulus of elasticity Gpa |
≥ 150 |
|||
|
solid phase line temperature ° C |
1410 ± 50 |
|||
|
Liquidus temperature ° C |
1440 ± 50 |
|||
|
Bonding strength of metal and porcelain |
≥ 25MPa |
|||
|
Specific Gravity |
8.6 g / cm3 |
|||
|
corrosion resistance |
The total amount of metal ions released into the specified solution should not exceed 200 μ g / cm2 |
|||
|
anti-tarnish |
anti-tarnish |
|||
Related products
-
OPTIMIZING CROSS CUT SAW MAXCUT F18S+SENSIT 005
Contact UsHigh speed optimization Timber cutting optimizing Cross-cut saw and precision cutting
Automation production line. -
Used NSC Schlumberger FM7N Spinning Machine
Contact UsThe company was established in Zhangjiagang, Jiangsu, China in 2005 .Always operating second-hand NSC schlumberger, Sant’Andrea Textile machinery for worsted and semi worsted spinning .
-
MA-(2~8MM)×1800MM Steel Coil Slitting Line
Contact UsMA-(2~8MM)×1800MM Steel Coil Slitting Line is mainly composed by the following components : uncoiler, guiding device
-
Waste plastic or Modified PE Pelletizing
Contact UsThe waste plastic or modified PE material is fed into the machine through a hopper. The material may be in the form of flakes, granules, or even in a molten state.
Reviews
There are no reviews yet.