BG7RH12
Product Name: BG7RH12Product grade: Injection molding grade.Product features: High-speed rail-specific fiber-reinforced nylon 6, with excellent mechanical properties.
BG7RH12-Typical molding process
|
Dry |
Drum wind oven: 100～120℃, 4～6h； Cycling warm air: 100～120℃,4～6h； Vacuum drying oven： 100～120℃,3～4h； |
|
Processing temperrature |
Feed section：235～250℃ Compressing section：245～270℃ Metering secion：250～270℃ |
|
Injection pressure |
50～100MPa |
|
Packing pressure |
30～70 Mpa |
|
Mold temperature |
60～90℃ |
|
Back pressure |
0～10Mpa |
BG7RH12
|
Test Item |
Test Standard |
Test Condition |
Unite |
Value |
|
Others |
||||
|
Ash Content |
ISO3451-1 |
620℃ |
% |
35 |
|
Melt Index |
ISO1133 |
250℃，2.16kg |
g/10min |
9 |
|
Density |
ISO1183 |
23℃ |
g/cm³ |
1.2 |
|
Mechanical |
||||
|
Flexural Strength |
ISO178 |
23℃，2mm/min |
MPa |
225 |
|
Flexural Modulus |
ISO178 |
23℃，2mm/min |
MPa |
7200 |
|
Tensile Strength |
ISO527 |
Type I spline,50mm/min |
MPa |
170 |
|
Elongation at Break |
ISO527 |
Type I spline,50mm/min |
% |
14 |
|
Charpy Notched Impact Strength |
ISO179/1eA |
23℃ |
kJ/m2 |
20 |
|
Charpy Unnotched Impact Strength |
ISO179/1eU |
23℃ |
kJ/m2 |
88 |
|
Thermal |
||||
|
Temperature of Deflection Under Load |
ISO75-2 |
0.45MPa |
℃ |
225 |
|
1.8MPa |
℃ |
205 |
||
|
Flammability |
||||
|
Flammability |
UL-94 |
1.6mm |
—— |
HB |
All is typical data, only for reference, not the permit of quality assurance.
Related products
-
Transparent Thick PET Sheet
Contact UsPET is a type of general-purpose thermoplastic.It offers excellent resistance to creep, high dimensional stability, and exceptional mechanical strength and can be cut to size, ready for immediate use.
-
Rubber Anti Vibration Mount Pad For Vehicle Rubber Automotive Shock Buffer Manufacturer From China
Contact UsCompression-molded vibration isolation pads. 75% energy absorption. Operating range: -30°C~110°C.UV-resistant compounds. MOQ 500pcs, 15-day lead time.
-
T700 chopped short carbon fiber
Contact UsChopped carbon fiber is a fibrous material made by cutting continuous carbon fiber tows into specific lengths.
-
Pickup Truck Bed
Contact UsSMC sheet molding compound for pickup truck beds is a semi-finished product made from unsaturated polyester resin reinforced with E-glass fibers, produced through precise mixing, impregnation, and thickening processes. This material can be used to produce various types of large structural components such as pickup truck bed bodies, bed liners, and tailgates, enabling lightweight solutions that replace traditional steel.